NEMA | C |
| CEI EN 60893 | PFCC201 | |
| Mil-I-24768 | 16 FBM | |
| DIN 7735 | HGW 2082 | |
| CNR CEI UNEL | Tipo F |
| Product made from coarse weave pure cotton fabric and phenolic resins. Has excellent workability and good dielectric characteristics. Great for the construction of medium and small silent gears, media, complex parts, etc. Can be easily sheared at room temperature up to a thickness of 1.5 to 2 mm, and after heating it at 100°C for greater thicknesses. |
| characteristics | conditioning | average value |
| Density | - | 1,40 g/cm³ |
| Maximum operating temperature | - | 120°C |
| Electrical resistance between plugs | E-24/100 | 104MOhm |
| Insulation resistance | E-24/100 | 103MOhm |
| Electric strength perpendicular (⊥) to laminations | d-03/90 | 5 KV/mm |
| Breakdown Voltage parallel (//) to laminations | d-25/90 | 8 KV |
| Dielectric constant (ε) | A | 5 |
| Comparative Tracking Index (C.T.I.) | A | 100 |
| Compressive strength perpendicular (⊥) to laminations | A | 3000 Kg/cm² |
| Compressive strength parallel (//) to laminations | A | 1700 Kg/cm² |
| Tensile strength | A | 800 Kg/cm² |
| Flexural strength | A | 1500 Kg/cm² |
| Impact strength (Charpy) | A | 35 Kg*cm/cm² |
| Rockwell hardness (scale F) | A | 60 |
| Water absorption | D-24/20 | 2% (≠ 1 mm) |
| Thermal conductivity | A | 0,2 W/m*K |
| conditioning | ||
| A | ambient conditions | |
| E-24/100 | After 24 hours in oven at 100°C | |
| D-24/20 | After 24 hours in water at 20°C | |
| d-03/90 | 1 minutes at 90°C in oil ≠ 3mm | |
| d-25/90 | 1 minutes at 90°C in oil ≠ 25mm |
| Note: The values in this datasheet are approximate and refer to the samples analyzed. The user is required to verify that the product is suitable for the use for which it is intended. |